Utilization of Clay and Fly Ash from Waste Industries Produced Lightweight Concrete Block for Load Bearing Wall

ศุธีรพันธ์ พันธ์เลิศ, พิทักษ์ เหล่ารัตนกุล, กฤษณา พูลสวัสดิ์


This research gained to using fly ash and silt from factories instead of cement, which reduced the amount of cement for production of lightweight aggregate concrete block. Calcium hydroxide (Ca(OH)2) and sodium hydroxide (NaOH) were catalysts, which added for some reactions, such as hydration, pozzolanic, and geopolymerization reaction. Ca2+, Si2+, O2-, OH- and Na2+ were increase ionization from the reactions. The formulation was 80% by weight of fly ash from paper factories and 5 molar of sodium hydroxide solution, which gained compressive strength 13.70 MPa and density 1,497 kg/m3 at 60 day of incubation. There may be available in general concrete industries.


Concrete Block, Waste Industries, Pozzolanic Reaction

Full Text:

PDF 6-13


ชัย จาตุรพิทักษ์กุล และ ปริญญา จินดา

ประเสริฐ. (2549). ปูนซีเมนต์ ปอซ

โซลาน และคอนกรีต. กรุงเทพฯ:


บุรฉัตร ฉัตรวีระ และ เพิ่มพล ศรีนวล.

(2555). การศึกษาสมบัติของมอร์



วารสารวิจัยและพัฒนา มจธ. ปีที่

(ฉบับที่ 2), หน้า 201 - 218.


(2533). มอก 57-2533 มาตรฐาน

ค อ น ก รีต บ ล็อ ก รับ น้า ห นัก .

ก รุง เ ท พ ม ห า น ค ร . ก ร ะ ท ร ว ง


American society for testing and

materials. (1995). “ASTM C

/C 109M-95: Standard

test method for compressive

strength of hydraulic cement

mortars (Using 2-in. or [50-

mm.] cube Specimens)”.

Annual book of ASTM

standards, Vol. 04.01, pp. 68 -72

American society for testing and

materials. (1995). “ASTM C 618-

a: Standard specification for

coal fly ash and raw or calcined

natural pozzzolan for use as a

meineral admixture in portland

cement concrete”. Annual book

of ASTM standards. Vol. 04.02, pp.

- 306.

Caijun S. and Robert L. D. (2000).

Pozzolanic reaction in the

presence of chemical activators

Part II. Reaction products and

mechanism. Cement and concrete

research, Vol. 30, pp. 607 - 613.

Day R.L. and Shi C. (1994). Relationship

between strength development

of lime–natural pozzolan pastes

and the blaine fineness of the

natural pozzolans. Cement and

concrete research, Vol. 24, pp.

- 1491.


  • There are currently no refbacks.

Copyright (c) 2017 วารสารวิชาการเทคโนโลยีอุตสาหกรรม : มหาวิทยาลัยราชภัฏสวนสุนันทา The Journal of Industrial Technology

Faculty of Industrial Technology Suan Sunandha Rajabhat University 1 U-tongnok Dusit Bangkok 10300  Tel. 66 2160 1438#22  E-mail. fit@ssru.ac.th